2022-07-28
Proyek |
Standar |
888 |
GL1805 |
GL1810 |
830CB |
GL1830 |
GLS805 |
GLS810 |
Tetembungane |
njaba |
Visual |
Cairan transparan kuning |
Cairan transparan kuning |
Cairan transparan kuning |
Cairan transparan kuning |
Cairan transparan kuning |
Cairan transparan kuning |
Cairan transparan kuning |
Chroma: < 2 |
Viskositas |
GB / T 22235-2008 |
12800mpa.s |
12100mpa.s |
12600mpa.s |
13200mpa.s |
12500mpa.s |
11500mpa.s |
11800mpa.s |
NDJ-5 (25℃) |
Rasio campuran |
nganggo resin epoksi 128 |
1:1 |
1:1 |
1:1 |
1:1 |
1:1 |
1:1 |
1:1 |
WAE 195 |
Wektu gel |
GB / T 12007.7-1989 |
3'40" |
3’45” |
8'50" |
25’20” |
25.30" |
3’55” |
9’10 |
Nilai rata-rata 5 pangukuran ing 30 ° C |
Kekuwatan geser |
GB / T 7124-2008 |
6,4mpa |
6,7mpa |
6,6mpa |
6,5mpa |
7,6mpa |
2,4mpa |
2,0 mpa |
Plate 25℃*4H (asor 50%) |
Kekuwatan Tensile |
GB / T 2567-2008 |
48 mpa |
47 mpa |
49mpa |
55mpa |
53mpa |
22mpa |
25mpa |
25℃*7 dina (kelembapan 50%) |
Kekuwatan komprèsi |
GB / T 2567-2008 |
63mpa |
62mpa |
62mpa |
64 mpa |
64 mpa |
38mpa |
39mpa |
25℃*7 dina (kelembapan 50%) |
TG |
ISO 11357-2:2013 |
34 |
33 |
30 |
30 |
28 |
34 |
33 |
25℃*7 dina (kelembapan 50%) |