Filamen Para-aramid digawe saka polikondensasi p-phenylene diamine lan terephthaloyl chloride. Munculé filamen kuning emas, Kapadhetan relatif kurang, lan kekuatan punika 5-6 kaping kawat baja. Nduwe retardansi nyala sing apik lan stabilitas termal. Bisa njaga bosok kinerja ing 200 ℃.
Spesifikasi utama yaiku 200D, 400D, 600D, 800D, 1000D, 1500D, lan 3000D, sing akeh digunakake ing ban, kabel optik, selang, produk karet, tali, rel kecepatan tinggi, aerospace, perlindungan pribadi, gesekan, sealing, lan lapangan liyane.
SF-2800
Kapadhetan linear |
Count |
Ngrusak ketabahan |
Kekuwatan sing rusak |
Elongati ing istirahat |
Modulus Young |
||||||||
Jinis |
Nominal |
Efektif |
|||||||||||
[denier] |
[dtex] |
[denier] |
[dtex] |
[ea] |
[g/d] |
[MPa] |
[cN/tex] |
[kgf] |
[N] |
[%] |
[g/d] |
[GPa] |
|
sedheng mbantah yam |
200 |
220 |
203 |
232 |
133 |
24 |
3050 |
212 |
4.8 |
48 |
2.8 |
860 |
109 |
400 |
440 |
404 |
460 |
267 |
24 |
3050 |
212 |
9.7 |
95 |
3.0 |
850 |
108 |
|
600 |
670 |
606 |
680 |
400 |
24 |
3050 |
212 |
14.5 |
143 |
3.1 |
800 |
102 |
|
Dhuwur denier yam |
800 |
880 |
807 |
903 |
536 |
23.5 |
2990 |
207 |
18.6 |
187 |
3.2 |
780 |
98 |
1000 |
1100 |
1010 |
1120 |
665 |
23.5 |
2990 |
207 |
23.7 |
233 |
3.2 |
720 |
92 |
|
1500 |
1650 |
1513 |
1678 |
1000 |
23.5 |
2990 |
207 |
35.6 |
342 |
3.3 |
720 |
92 |
|
3000 |
3330 |
3030 |
3360 |
2000 |
23 |
2930 |
203 |
69.7 |
683 |
3.6 |
650 |
83 |
|
Standar |
ASTM D1907 Pilihan 6 |
ASTM D885 |
SF-6800
Kapadhetan linear |
Count |
Ngrusak ketabahan |
Kekuwatan sing rusak |
Elongation ing break |
Modulus Young |
|||||||
Nominal |
|
Effeaktif |
|
|
|
|
|
|
|
|
|
|
[denier] |
[dtex] |
[denier] |
[dtex] |
[ea] |
[g/d] |
[MPa] |
[cN/tex] |
[kgf] |
[N] |
[%] |
[g/d] |
[GPa] |
600 |
670 |
606 |
680 |
400 |
27.0 |
3430 |
238 |
16.4 |
160 |
3.3 |
850 |
108 |
840 |
930 |
850 |
940 |
665 |
26.5 |
3370 |
234 |
22.5 |
221 |
3.4 |
800 |
102 |
1000 |
1110 |
1010 |
1120 |
665 |
26.5 |
3370 |
234 |
26.8 |
262 |
3.5 |
800 |
102 |
1500 |
1670 |
1515 |
1680 |
1000 |
26.0 |
3300 |
229 |
39.4 |
386 |
3.5 |
780 |
99 |
2820 |
3140 |
2840 |
3160 |
2000 |
25.5 |
3240 |
225 |
72.4 |
710 |
3.8 |
710 |
90 |
ASTM D1907 Pilihan 6 |
ASTM D885 |
SF-4800
Kapadhetan linear |
Ngrusak ketabahan |
Kekuwatan sing rusak |
Elongation ing break |
URUTANE |
Modulus Young |
|||||||||
0,5% |
1.0% |
|||||||||||||
[dtex] |
[g/d] |
[cN/tex] |
[kgf] |
[N] |
[%] |
[cN/dtex] |
[N] |
[cN/tex] |
[N] |
[g/d] |
[GPa] |
|||
1610 |
23.0 |
203 |
32.9 |
323 |
2.5 |
3.8 |
61 |
7.5 |
84 |
905 |
115 |
|||
3220 |
22.5 |
199 |
64.4 |
631 |
2.5 |
3.6 |
116 |
7.5 |
167 |
905 |
115 |
|||
6440 |
22.0 |
194 |
126 |
1234 |
2.7 |
3.6 |
232 |
7.5 |
335 |
866 |
110 |
|||
8050 |
22.0 |
194 |
157 |
1543 |
2.8 |
3.5 |
282 |
7.5 |
419 |
866 |
110 |
|||
ASTM D1907 Pilihan 6 |
ASTM D885 |